Influencing Factors on the Interface Microhardness of Lightweight Aggregate Concrete Consisting of Glazed Hollow Bead

Influencing Factors on the Interface Microhardness of Lightweight Aggregate Concrete Consisting of Glazed Hollow Bead

Blog Article

Lightweight aggregate concrete consisting of glazed hollow bead (GHB) as lightweight aggregate is studied for the influence of nanosilica (NS) content, prewetting time for GHB, water-cement ratio, and curing humidity, on the interface structure between GHB and cement paste.This research analyzed the influences of various factors on the interface zone structure by measuring microhardness (HV) and hydration degree of cement paste (HD) nearby the interface zone (1 mm) between GHB and cement paste at different ilootpaperie periods of aging.Due to the sampling limitation, the interface zone in this test is within 1 mm away from the surface of lightweight aggregate.The camo iphone se case HD of cement paste was determined through chemically combined water (CCW) test.The results were expected to reflect the influence of various factors on the interface zone structure.

Results showed that the rational control of the four factors studied could fully mobilize the water absorption and desorption properties of GHB to improve the characteristics of the interfacial transition zone.